Measures for prolonging service life of refractory lining of

Extending the service life of refractory materials for glass kiln, that is, extending the kiln age of the kiln, can increase the medium melting rate of the kiln, reduce non-production time and repair kiln costs, thereby increasing the output value and benefits of the plant. Can be considered from the following links.
 
1. In the initial design of the glass kiln lining, the structure and material selection should be reasonably designed according to the thermal principle and design principle, especially to avoid or reduce the scouring of the flame. For example, the chest wall should try to avoid the scouring of the blasting flame. The top of the furnace mouth and the regenerator should be prevented from scouring. The holes in the kiln should prevent the overflow of the flame; properly reduce the thermal intensity of the flame space and reduce the temperature of the inner surface of the kiln; reduce the flushing of the glass, such as minimizing Horizontal seams to avoid local overheating. Do not have eddy currents or dead angles in the smoke stroke to avoid local overheating and burn the kiln. 2. During the construction process, the construction rules and masonry requirements should be observed to ensure the construction quality. In particular, it is necessary to pay attention to the careful selection of bricks. If there are cracks in the corners, try not to use them. Try to process the surface of the bricks that are in contact with the flame or glass. Avoid damage to the bricks.